LC-68 Matt Curing Agent

Delivery term:The date of payment from buyers deliver within days
  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Shandong

  • Validity to:

    Long-term effective

  • Last update:

    2017-12-30 23:32

  • Browse the number:

    190

Send an inquiries
+
Yantai Longcai Advanced Materials Co.,Ltd
Contactaixin:

Contactaixin:

lingyufenmo(Mr.)  

Email:

telephone:

phone:

Area:

Shandong

Address:

No.18 Hangzhou Rd., Haiyang Development Zone, Haiyang 265100, China

Website:

http://www.longcai-group.com/ http://www.interview-training-uk.com/com/lingyufenmo/

+

Specialized in producing high-quality lc-68 matt curing agent, LONGCAI is one of the best lc-68 matt curing agent manufacturers and suppliers in China. Equipped with a professional factory, welcome to buy CE certification products at good price from our company.

General Description


LC-68 is a widely used in interior matting powder coatings.
Excellent gloss stability.
· Can get dead matting gloss:less than 5 gloss unit
· Good mechanical performance
· Provide wide gloss range from 3~60%
· LC-68 react with epoxy ratio is 1:9 or 1:10


Extrusion & Application Conditions


Extruder:Lingyu SLJ-20

Zone I temp:85~105℃

Zone II temp:100~120℃

Screw speed:400~500rpm

Panel:0.5mm pre-treated cold-rolled steel

Spray gun:Lingyu JP-80

Voltage:60~90kV

Curing cycles:10 min. @ 200℃


Packaging


· White PE bag, N.W.25kg/bag


Storage


The product can be stably stored for at least one year when kept in closed containers in a dry place at temperature below 30℃.Avoid exposure to direct sunlight.


Product Specifications


Property Range Test Method
Appearance White powder VisuaVisuall
Melting Range (℃) 222~227 ISO11357-1
Water content <1.0% Longcai method



Starting Formulation



Property Range
Epoxy resin 300.0
LC-68 33.0
Titanium dioxide 150.0
LC-88 Flow agent 5.0
Benzoin 3.0


Film Properties



Item Result Test Method
Film thickness, μm approx. 60 ASTM D1186
Gloss @ 60o, % 3 unit ASTM D523
Direct/reverse impact, inch lbs 40/40 ASTM D2794
1/8" Conical mandrel pass ASTM D522
Adhesion(cross cut) 5B ASTM D3359
Pencil hardness(Mar) H ISO 15184-98